I-Ferrite Magnet
I-SinteredI-Ferrite MagnetIzakhiwo Zomzimba | |||||||||
Ibanga | Remanence | Umfundisi Temp. Coef. OkaBr | Amandla Okuphoqa | I-Intrinsic Coercive Force | Umfundisi Temp.-Coeff. Kwe Hcj | Ubukhulu. Umkhiqizo Wamandla | Ubukhulu. Izinga Lokushisa Lokusebenza | Ukuminyana | |
I-Br (KGs) | Hcb (WENA) | Hcj (WENA) | (BH) ubukhulu. (MGOe) | g/cm³ | |||||
Y10T | 2.0-2.35 | -0.20 | 1.57-2.01 | 2.64-3.52 | +0.30 | 0.8-1.2 | 250 ℃ | 4.95 | |
Y20 | 3.2-3.8 | -0.20 | 1.70-2.38 | 1.76-2.45 | +0.30 | 2.3-2.8 | 250 ℃ | 4.95 | |
Y22H | 3.1-3.6 | -0.20 | 2.77-3.14 | 3.52-4.02 | +0.30 | 2.5-3.2 | 250 ℃ | 4.95 | |
Y23 | 3.2-3.7 | -0.20 | 2.14-2.38 | 2.39-2.89 | +0.30 | 2.5-3.2 | 250 ℃ | 4.95 | |
Y25 | 3.6-4.0 | -0.20 | 1.70-2.14 | 1.76-2.51 | +0.30 | 2.8-3.5 | 250 ℃ | 4.95 | |
Y26H | 3.6-3.9 | -0.20 | 2.77-3.14 | 2.83-3.21 | +0.30 | 2.9-3.5 | 250 ℃ | 4.95 | |
Y27H | 3.7-4.0 | -0.20 | 2.58-3.14 | 2.64-3.21 | +0.30 | 3.1-3.7 | 250 ℃ | 4.95 | |
Y28 | 3.7-4.0 | -0.20 | 2.20-2.64 | 2.26-2.77 | +0.30 | 3.3-3.8 | 250 ℃ | 4.95 | |
Y30 | 3.7-4.0 | -0.20 | 2.20-2.64 | 2.64-2.77 | +0.30 | 3.3-3.8 | 250 ℃ | 4.95 | |
Y30H-1 | 3.8-4.0 | -0.20 | 2.89-3.46 | 2.95-3.65 | +0.30 | 3.4-4.1 | 250 ℃ | 4.95 | |
Y30BH | 3.8-3.9 | -0.20 | 2.80-2.95 | 2.90-3.08 | +0.30 | 3.4-3.7 | 250 ℃ | 4.95 | |
Y30-1 | 3.6-4.0 | -0.20 | 1.70-2.14 | 1.76-2.51 | +0.30 | 2.8-3.5 | 250 ℃ | 4.95 | |
Y30BH-1 | 3.8-4.0 | -0.20 | 2.89-3.46 | 2.95-3.65 | +0.30 | 3.4-4.0 | 250 ℃ | 4.95 | |
Y30H-2 | 3.95-4.15 | -0.20 | 3.46-3.77 | 3.90-4.21 | +0.30 | 3.5-4.0 | 250 ℃ | 4.95 | |
Y20-2 | 3.95-4.15 | -0.20 | 3.46-3.77 | 3.90-4.21 | +0.30 | 3.5-4.0 | 250 ℃ | 4.95 | |
Y32 | 4.0-4.2 | -0.20 | 2.01-2.38 | 2.07-2.45 | +0.30 | 3.8-4.2 | 250 ℃ | 4.95 | |
Y33 | 4.1-4.3 | -0.20 | 2.77-3.14 | 2.83-3.21 | +0.30 | 4.0-4.4 | 250 ℃ | 4.95 | |
Y35 | 4.0-4.1 | -0.20 | 2.20-2.45 | 2.26-2.51 | +0.30 | 3.8-4.0 | 250 ℃ | 4.95 | |
Qaphela: · Sihlala sifana nangenhla ngaphandle uma sishiwo yikhasimende. Izinga lokushisa le-Curie ne-temperature coefficient yenzelwe inkomba kuphela, hhayi njengesisekelo sesinqumo.· Izinga lokushisa eliphakeme kakhulu likazibuthe liyashintsha ngenxa yesilinganiso sobude nobubanzi kanye nezici zendawo. |
Inzuzo:
Njengoba kuvamile kuma-oxide ceramics, omagnethi be-ferrite abaqinile babonisa ukuziphatha okungahambisani nomswakama, izincibilikisi, izixazululo ze-alkali,
ama-acids abuthakathaka, usawoti, amafutha kanye nezinto ezingcolisa igesi. Ngokuvamile, omazibuthe be-ferrite abaqinile bangasetshenziswa ngaphandle kokuvikela ukugqwala okwengeziwe.
Isici:
Ngenxa yokuqina kwawo okukhulu (6-7 Mohs), omagnethi beFerrite bashwabene futhi bayazwela lapho bengqongqoza noma begotshwa. Ngesikhathi sokucubungula, kufanele zenziwe ngomshini ngamathuluzi edayimane. Amazinga okushisa asebenzayo anozibuthe be-ferrite ngokuvamile aphakathi kuka -40ºC no-250ºC.
Isicelo:
Kusetshenziswa umumo ohlukile kubunjiniyela be-othomotive, njengokuzenzakalelayo nokulawula ukulinganisa. Ezinye izinhlelo zokusebenza ezifana nemishini kagesi ye-Automobile (ama-wiper, i-sit chair motor), Ukufundisa, i-Door absorber, ibhayisikili leMagnetic kanye nesitulo sokubhucunga, njll.
Namuhla, ama-ferrite aqinile amelela ingxenye enkulu kakhulu yamagnethi ahlala njalo akhiqizwa. Ngokungafani nozibuthe be-AlNiCo, ama-ferrite aqinile abonakala ngokuminyana okuguquguqukayo kodwa amandla enkambu aphezulu aphoqelelayo. Lokhu kubangela ukuma okuyisicaba ngokuvamile kwezinto. I-Barium ferrite ne-strontium ferrite ihlukaniswa kuye ngokuthi iqala kanjani.
Wonke amanani ashiwo anqunywa kusetshenziswa amasampula ajwayelekile ngokuya nge-IEC 60404-5. Ukucaciswa okulandelayo kusebenza njengamanani okubhekisela futhi kungase kuhluke.